AFM characterization of bovine enamel and dentine after acid-etching.

star_border
     Loading your article ...      Welcome to Your Next Discovery   
PDF
Article Details
Authors
Roberto Pizarro Sanches, Choyu Otani, Alvaro José Damião, Walter Miyakawa
Journal
Micron (Oxford, England : 1993)
PM Id
19138525
DOI
10.1016/j.micron.2008.12.001
Table of Contents
Abstract
Abstract
Teeth are constituted mainly of hydroxyapatite molecules (Ca10(PO4)6(OH)2), grouped in different microstructural arrangements, depending on the dental layer considered (enamel or dentine). In the present work, these dental microstructural arrangements were characterized by atomic force microscopy. Enamel and dentine samples were cut from freshly extracted bovine incisor teeth. After metallographic polishing, the dental surfaces were etched with lactic acid (113.8 mmol/L, pH 3.3). Three etching times were tested: 1, 3 and 5 min. Atomic force micrographs showed that 1 min of etching time was effective to remove the smear layer, polishing debris and scratches, and display the characteristics of interest for both enamel and dentine. Although the bovine dental enamel rod cross-section presented keyhole-like shape, its measured dimensions (8.8 mm of major axis and 3.7 mm of minor axis) exhibited an insignificant discrepancy from human prisms diameters. Bovine dentinal tubules displayed larger mean diameters (4.0 mm) and a lower density ( 17,100 tubules/mm) than human dentine, suggesting that the use of bovine dentine as a substitute for human dentine in resin adhesion investigations should be reconsidered. Apatite nanoparticles presented a mean radius (22–23 nm) considerably smaller than that of human teeth. 2008 Elsevier Ltd. All rights reserved.
 
Article Images (0)